In the course of using the

stainless steel butterfly valves in corrosion phenomenon. After dyeing try face, heat treatment, microstructure analysis, face, such as SEM test analysis, found the key factors for material corrosion because of materials along the grain boundary carbide precipitation form poor chrome area, causing no rust stainless steel butterfly valve. Material for CF8M stainless steel butterfly in corrosion phenomena appeared in the process of use. Austenitic stainless steel after normal heat treatment, the organization shall be the austenite at room temperature, corrosion resistant performance is very good. In order to analyze the corrosion cause of butterfly Industrial Valves, on which the sample is analyzed. The material of the stainless steel butterfly valves for austenitic stainless steel, nickel chromium this kind of material is generally used in solid solution state. At room temperature, its organization for austenitic austenitic stainless steel in a wide range of corrosive medium, especially the atmosphere with good corrosion resistance. Comprehensive analysis: the reason for the stainless steel butterfly valve corrosion test results, to determine the organization is not precipitate phase in the butterfly Industrial Valves material & sigma; Phase, therefore, the corrosion phenomenon of the butterfly Industrial Valves is not by & sigma; Phase; Determined by SEM observation that the organization of the butterfly valve of chromium carbides precipitate phase in the, the eutectic distribution along the grain boundary. EDS analysis results show that this kind of distribution on the grain boundary carbides chromium content is significantly higher than the substrate. This kind of carbide M23C6 type. With the precipitation of carbide, and lack of chromium diffusion added, in the form of chromium carbide along the austenite grain boundary precipitation, form poor chrome area around carbide, austenitic stainless steel grain boundaries are easy to corrode. Along the grain boundary precipitation of carbide is the main cause of butterfly valve rust; After solid solution treatment of austenitic stainless steel, because most of the carbide was dissolved in high temperature heating, austenitic saturation in a large amount of carbon and chromium, and fixed by the subsequent rapid cooling, the corrosion resistance of material has a business. So should strictly control the heat treatment process, the solid solution treatment when the workpiece heated to a high return, the carbide dissolved in full, and then rapidly cooling, to get uniform austenite organization. After solid solution treatment, if use the slow cooling, the cooling process of chromium carbide along the grain boundary precipitates, which results in the decrease of the corrosion resistance of materials.

Shenzhen Mech Valve Trading Co., Ltd. is different from other companies as we provide timely and unique services to our respected clients.
For decades, Shenzhen Mech Valve Trading Co., Ltd. has searched for and found a number of secrets to help customers through out the world to achieve resilient seated valve by providing useful and efficient solutions. Go to Mech Valve to learn about some of those secrets.
To find a qualified at reasonable price, contact Shenzhen Mech Valve Trading Co., Ltd. at Mech Valve, a professional provider and tell them what you envision for your double flanged gate valve.
Shenzhen Mech Valve Trading Co., Ltd. needs to ensure we're resolving customer issues as quickly as possible. By doing so, it leads to positive customer experiences and brand loyalty.
Shenzhen Mech Valve Trading Co., Ltd. can assure that it is one of the best products in the market at present.